Shree Digvijay Cement  
Shree Digvijay Cement Company Limited
A Cimpor Group Company
About Us business products t.a.s.c. investors media career group site
 Other Products :
Ordinary Portland Cement 53 grade (OPC) as per BIC / BC / ASTM / SLS standards
Oridinary Portland Cement 43 grade (OPC)
Birla Plus Cement (Portland Pozzolana Cement)
Railway Sleeper Manufacturing Cement (53-S Grade OPC)
Oil Well Cement Class 'G' HSR (as per API specifications)
Our Customers
domestic
international
products
KAMAL PORTLAND POZZOLANA CEMENT STAR STRENGTH – STAR PERFORMANCE
Home Contact Us Search Site Map

KAMAL PPC is a high quality premium composite cement. It is a new generation cement containing high reactive Silica in its composition in measured quantity in order to improve impermeability. It continues to gain strength and provides long term durability to concrete structure.
KAMAL PPC is 3 in 1 Cement because it is a Low Heat, Alkali – Sulphate Resistant & Corrosion Protective Cement.
ADVANTAGES
Higher durability of concrete structure due to less permeability of water.  
Better workability.
Low heat of hydration.
Less Cracks.
Higher resistance towards attacks of alkalies, sulphates, chlorides & chemicals.
Provide Consistent gain of strength & long term durability.
Because of finer & improved particle size distribution, PPC has better cohesion with aggregates and it makes more dense concrete.
Provide better surface finish.
IDEAL APPLICATIONS
Mass concrete works – Dams & Canals
Residential, Commercial & Industrial Buildings
Effluent, Sewerage & Water treatment Plants
Plaster & Brick work.
Roads, Runways, Culverts etc.

BIS SPECIFICATIONS AND SDCC NORMS OF KAMAL PPC (Portland Pozzolana Cement)

Sr.No. Description Unit Requirement As Per IS 1489 ( P- 1 ) 1991 SDCC Norms
A) CHEMICAL COMPOSITION
1. Insoluble Residues(IR) % X*+ (4.0(100-X)/100) 14.00 Min.
2. Magnesium Oxide(MgO) % 6.0 Max 2.00 Max.
3. Sulphuric Anhydride(SO3) % 3.0 Max. 2.75 Max.
4. Loss on Ignition(LOI) % 5.0 Max 3.0 Max.
B) PHYSICAL PROPERTIES
1. Specific Surface m2/kg 300 Min. 340 Min.
2. Soundness (Expansion)  
  a) By Le-Chatelier mm 10.0 Max. 3.0 Max.
b) By Autoclave % 0.8 Max. 0.2 Max
3. Setting Time  
  a) Initial Set Minute 30 Min. 45 Min.
b) Final Set Minute 600 Max. 275Max.
4. Compressive Strength  
  a) 3 days MPa 16 Min. 30Min.
b) 7 days MPa 22 Min. 40 Min.
c) 28 days MPa 33 Min. 55 Min.
5. Drying Shrinkage % 0.15 Max. 0.10 Max.
Note: * X = Declared percentage of Pozzolana in Portland Pozzolana Cement by weight. Pozzolana constituent shall not be less than 15% and more than 35% by mass of PPC.